Information recording medium

ABSTRACT

An information recording medium showing a high light-resistance has a recording layer containing a dye compound having the following formula (I-1) or (I-2):  
                 
 
     in which each of A 1 , A 2 , B 1  and B 2  is a substituent; each of Y 1  and Z 1  is a group of atoms required for forming a carbon ring or a heterocyclic ring; each of E and G is a group of atoms required for forming a conjugated double bond chain; X 1  is ═O, ═NR or ═C(CN) 2 , wherein R is a substituent; X 2  is —O, —NR or —C(CN) 2 , wherein R is a substituent; each of L 1 , L 2 , L 3 , L 4  and L 5  is a methine group which may have a substituent; M k+  is an onium ion containing a positively charged onium atom to which no hydrogen atom is attached; each of m and n is 0, 1 or 2; each of x and y is 0 or 1; and x is an integer of 1 to 10.

FIELD OF THE INVENTION

[0001] This invention relates to an information recording medium on which information can be recorded by means of a laser beam having a high energy density, and a dye compound which is favorably utilized for preparing the information recording medium.

BACKGROUND OF THE INVENTION

[0002] The recordable compact disc (CD-R), on which information can be recorded only once, is widely used, for instance, as a large capacity computer data disc.

[0003] The optical disc of CD-R type generally comprises a disc-shaped substrate (support) and a recording layer provided thereon. The disc substrate comprises a transparent material such as synthetic resin. The recording layer comprises a metal or a semi-metal such as Bi, Sn, In or Te, or alternatively a dye such as a cyanine dye, a metal-complex dye, or a quinone dye. A light-reflecting layer and a protective layer may be superposed in order on the recording layer. The light-reflecting layer and the protective layer can be made of gold and resin, respectively.

[0004] On the CD-R, the writing (recording) and reading (reproducing) can be performed in the following manner. The laser beam (usually used wavelength is 780 nm) modulated by information is applied to the recording layer of the CD-R through the substrate. The recording layer alters its optical characteristics in the area where the laser beam has been applied, to produce a chemical or physical change such as production of pit. The reading of the recorded information can be performed by sequentially applying a laser beam on the recording layer of the CD-R through the substrate and detecting a light reflected on the CD-R.

[0005] At present, most of the recording layer of CD-R utilizes a light-sensitive dye as the recording material, because the recording dye layer can be easily formed by a coating method and shows a high sensitivity, as compared with the recording metal layer. However, the dye layer has such disadvantages as low light-resistance and low heat resistance. Therefore, it has been desired to develop a recording layer having high durability against light and heat, as well as having high recording and reproducing characteristics.

[0006] Japanese Patent Provisional Publication No. 63-209995 describes an optical disc which has a recording layer comprising an oxonol dye. According to the description of publication, such optical disc maintains stable recording and reproducing characteristics for a long time. The publication discloses an oxonol dye compound having an ammonium ion in the form of an inner salt.

[0007] The inventors have found that the optical disc having the recording layer of the above oxonol dye exhibits insufficient light-resistance, while the disc has relatively improved characteristics in view of heat resistance and durability for repeated reproducing. Therefore, such optical disc often causes troubles in reproducing process after long exposure to light such as sunlight.

[0008] Accordingly, it is an object of the present invention to provide an information recording medium having stable recording characteristics and particularly high light-resistance to maintain satisfactory recording characteristics for a long time.

[0009] It is another object of the present invention to provide a new oxonol dye compound favorably employable for preparing the information recording medium having stable recording characteristics.

SUMMARY OF THE INVENTION

[0010] The present invention resides in an information recording medium comprising a support and a recording layer provided thereon on which information can be recorded by means of a laser beam, wherein said recording layer contains a dye compound having the below-mentioned formula (I-1) or (I-2):

[0011] in which each of A¹, A², B¹ and B² independently represents a substituent group; each of Y¹ and Z¹ independently represents a group of atoms required for forming a carbon ring or a heterocyclic ring; each of E and G independently represents a group of atoms required for forming a conjugated double bond chain; X¹ represents ═O, ═NR or ═C(N)₂/wherein R is a substituent group; X² represents —O, —NR or —C(CN)₂, wherein R is a substituent group; each of L¹, L², L³, L⁴ and L³ independently represents a methine group which may have a substituent group; M^(k+) represents an onium ion containing a positively charged onium atom to which no hydrogen atom is attached; each of m and n independently is an integer of 0, 1 or 2; each of x and y independently is an integer of 0 or 1; and x is an integer of 1 to 10.

[0012] The invention further resides in a new oxonol compound having the below-mentioned formula (IV-1) or (IV-2):

[0013] in which each of A³, A⁴, B³ and B⁴ independently represents a substituent group selected from the group consisting of a linear, branched or cyclic alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, an aryl group having 6 to 18 carbon atoms, an aralkyl group having 7 to 18 carbon atoms, an acyl group having 2 to 18 carbon atoms, an alkylsulfonyl group having 1 to 18 carbon atoms, an arylsulfonyl group having 6 to 18 carbon atoms, an alkylsulfinyl group having 1 to 18 carbon atoms, an alkoxycarbonyl group having 2, to 18 carbon atoms, an aryloxycarbonyl group having 7 to 18 carbon atoms; an alkoxy group having 1 to 18 carbon atoms, an aryloxy group having 6 to 18 carbon atoms, an alkylthio group having 1 to 18 carbon atoms, an arylthio group having 6 to 10 carbon atoms, an acyloxy group having 2 to 18 carbon atoms, a sulfonyloxy group, a carbamoyloxy group, an amino group, a carbamoyl group, a sulfamoyl group, a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxyl group, and a 4- to 7-membered heterocyclic group, wherein these substituent groups may be substituted with at least one group selected from those consisting of the above-mentioned substituent groups;

[0014] each of Y² and Z² independently represents a group of atoms required for forming a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring, which may be substituted with at least one group selected from those consisting of the substituent groups described for A³, A⁴, B¹ and B⁴ and may be fused with a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring;

[0015] each of L⁶, L⁷, L⁸, L⁹ and L¹⁰ independently represents a methine group which may have one or two substituent groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴;

[0016] M²⁺ represents a quaternary ammonium ion; and

[0017] each of m1 and n1 independently represents an integer of 0, 1 or 2.

[0018] In contrast to the known oxonol dye compounds, the new oxonol dye compound of the invention comprises an onium salt in which an onium atom has no hydrogen atoms thereon (quaternary ammonium salt is particularly preferred). The inventors have found that the new oxonol dye compound enhances light-resistance to provide the information recording medium.

DETAILED DESCRIPTION OF THE INVENTION

[0019] The preferred embodiments of the invention are as follows:

[0020] (1) M^(k+) in the formula (I-1) or (I-2) is a quaternary ammonium ion.

[0021] (2) k in the formula (I-1) or (I-2) is an integer of 0 to 4.

[0022] (3) k in the formula (I-1) or (I-2) is 2.

[0023] (4) M^(k+) is an onium ion of the below-mentioned formula (II):

[0024] in which each of R¹ and R² independently represents a group selected from the group, consisting of an alkyl group, an alkenyl group, an alkynyl group, an aryl group or a heterocyclic group; each of R³ and R⁴ independently represents a substituent group; or each set of R¹ and R³, R² and R⁴, or R³ and R⁴ can be combined to form a ring; each of q1 and r1 independently is an integer of 0 to 4; provided that plural R³ and plural R⁴ are the same as or different from each other in the case that q1 and r1 are 2 or more, respectively.

[0025] (5) M^(k+) is an onium ion of the below-mentioned formula (III):

[0026] in which each of R⁵ and R¹ independently represents a group selected from the group consisting of an alkyl group, an alkenyl group, an alkynyl group, an aryl group and a heterocyclic group; each of R⁷ and R⁸ independently represents a substituent group; or each set of R⁵ and R⁶, R⁵ and R⁷, R¹ and R⁸, or R⁷ and R¹ can be combined to form a ring; each of q2 and r2 independently is an integer of 0 to 4; provided that plural R⁷ and plural R⁸ are the same as or different from each other in the case that q2 and r2 are 2 or more, respectively.

[0027] (6) In the formula (I-1) or (I-2), each of m and n is 1; m is 0, while n is 2; or m is 2, while n is 2.

[0028] (7) In the formula (I-1) or (I-2), X¹ is ═O and X² is —O.

[0029] (8) A light-reflecting layer is provided on the recording layer.

[0030] (9) A protective layer is provided on the light-reflecting layer.

[0031] (10) M²⁺ in the formula (IV-1) or (IV-2) is an ion having the below-mentioned formula (V):

[0032] in which each of R¹¹ and R¹² independently represents a group selected from the group consisting of an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³, A⁴ ₁, B³ and B⁴ of the formulas (IV-1) or (IV-2); each of R and R¹⁴ independently represents a substituent group selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹¹ and R¹³, R¹² and R¹⁴, or R¹³ and R¹⁴ can be combined to form a 4- to 7-membered ring; each of q3 and r3 independently is an integer of 0 to 4; provided that plural R¹³ and plural R¹⁴ are the same as or different from each other in the case that q3 and r3 are 2 or more, respectively.

[0033] (11) M²⁺ in the formula (IV-1) or (IV-2) is an ion having the below-mentioned formula (VI):

[0034] in which each of R¹⁵ and R¹⁶ independently represents a group selected from the group consisting of an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³ ₁, A⁴ B³ and B⁴ of the formulas (IV-1) or (IV-2); each of R¹⁷ and R¹⁸ independently represents a substituent group selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹⁵ and R¹⁶, R¹⁵ and R¹⁷, R¹⁶ and R¹⁸, or R¹⁷ and R¹⁸ can be combined to form a 4- to 7-membered ring; each of q4 and r4 independently is an integer of 0 to 4; provided that plural R¹⁷ and plural R¹⁸ are the same as or different from each other in the case that q4 and r4 are 2 or more, respectively.

[0035] (12) In the formula (IV-1) or (IV-2), each of m1 and n1 is 1; m1 is 0, while n1 is 2; or m1 is 2, while n1 is 0.

[0036] (13) In the formula (IV-1) or (IV-2), each of the carbon ring and the heterocyclic ring for the group of atoms represented by Y² or Z² is pyrazolone ring, ring of thiobarbituric acid, ring of barbituric acid, indandione ring, or hydroxyphenalenone ring.

[0037] The information recording medium of the invention and the new oxonol compound are further described below.

[0038] The information recording medium of the invention is characterized by comprising the recording layer containing the oxonol dye compound having the aforementioned formula (I-1) or (I-2).

[0039] The oxonol dye compound of the invention is described below in more detail.

[0040] The oxonol dye compound favorably employable for the invention consists essentially of an anion part (dye component) and a cation part (onium component).

[0041] First, the anion part is described.

[0042] Examples of the substituent groups represented by A¹, A², B¹ and B² in the above formulas include following groups:

[0043] an alkyl group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups and which may form straight-chain or branched-chain or cyclic structure (e.g., methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl, t-butyl, cyclohexyl, methoxyethyl, ethoxycarbonylethyl, cyanoethyl, diethylaminoethyl, hydroxyethyl, chloroethyl, acetoxyethyl, and trifluoromethyl);

[0044] an aralkyl group of 7-18 (preferably 7-12) carbon atoms which may have one or more substituent groups (e.g., benzyl, and carboxybenzyl);

[0045] an alkenyl group of 2-18 (preferably 2-8) carbon atoms (e.g., vinyl);

[0046] an alkynyl group of 2-18 (preferably 2-8) carbon atoms (e.g., ethynyl);

[0047] an aryl group of 6-18 (preferably 6-10) carbon atoms which may have one or more substituent groups (e.g., phenyl, 4-methylphenyl, 4-methoxyphenyl, 4-carboxyphenyl, and 3,5-dicarboxyphenyl);

[0048] an acyl group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., acetyl, propionyl, butanoyl, and chloroacetyl);

[0049] an alkylsulfonyl or arylsulfonyl group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methanesulfonyl and p-toluenesulfonyl);

[0050] an alkylsulfinyl group of 1-18 (preferably 1-8) carbon atoms (e.g., methanesulfinyl, ethanesulfinyl, and octanesulfinyl);

[0051] an alkoxycarbonyl group of 2-18 (preferably 2-8) carbon atoms (e.g., methoxycarbonyl, and ethoxycarbonyl);

[0052] an aryloxycarbonyl group of 7-18 (preferably 7-12) carbon atoms (e.g., phenoxycarbonyl, 4-methylphenoxycarbonyl, and 4-methoxyphenylcarbonyl);

[0053] an alkoxy group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methoxy, ethoxy, b-butoxy, and methoxyethoxy);

[0054] an aryloxy group of 6-18 (preferably 6-10) carbon atoms which may have one or more substituent groups (e.g., phenoxy and 4-methoxyphenoxy);

[0055] an alkylthio group of 1-18 (preferably 1-8) carbon atoms (e.g., methylthio and ethylthio);

[0056] an arylthio group of 6-10 carbon atoms (e.g., phenylthio);

[0057] an acyloxy group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., acetoxy, ethylcarbonyloxy, cyclohexylcarbonyloxy, benzoyloxy, and chloroacetyloxy);

[0058] a sulfonyloxy group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methanesulfonyl);

[0059] a carbamoyloxy group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., methylcarbamoyloxy and diethylcarbamoyloxy);

[0060] an amino group having 0-18 (preferably 0-8) carbon atoms which may have one or more substituent groups (e.g., non-substituted amino, methylamino, dimethylamino, diethylamino, anilino, methoxyphenylamino, chlorophenylamino, morpholino, piperidino, pyrrolidino, pyridylamino, methoxycarbonylamino, n-butoxycarbonylamino, phenoxycarbonylamino, methylcarbamoylamino, phenylcarbamoylamino, ethylthiocarbamoylamino, methylsufamoylamino, phenylsufamoylamino, acetylamino, ethylcarbonylamino, ethylthiocarbonylamino, cyclohexylcarbonylamino, benzoylamino, chloroacetylamino, methanesulfonylamino, and benzenesulfonylamino);

[0061] a carbamoyl group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., non-substituted carbamoyl, methylcarbamoyl, ethylcarbamoyl, n-butylcarbamoyl, t-butylcarbamoyl, dimethylcarbamoyl, morpholinocarbamoyl, and pyrrolidinocarbamo-yl);

[0062] a sulfamoyl group having 0-18 (preferably 0-8) carbon atoms which may have one or more substituent groups (e.g., non-substituted sulfamoyl, methylsulfamoyl, and phenylsulfamoyl);

[0063] a halogen atom (e.g., fluorine, chlorine, and bromine); hydroxyl group; nitro group; cyano group; carboxyl group; and

[0064] a heterocyclic group (oxazole, benzoxazole, thiazole, benzothiazole, imidazole, benzoimidazole, indolenine, pyridine, sulfolane, furan, thiophene, pyrazol, pyrrole, chroman, and coumarin).

[0065] Each of the substituent groups represented by A¹ and A² preferably has Hammett's substituent constant (σ_(p)) of not less than 0.2. The values of Hamnrett's substituent constant (σ_(p)) are set forth in, for instance, Chem. Rev., 91, 165(1991). Examples of the particularly preferred substituent groups include cyano group, nitro group, alkoxycabonyl group, acyl group, carbamoyl group, sulfamoyl group, alkylsufonyl group, and arylsulfonyl group. Examples of the preferred substituent groups represented by B¹ and B² include alkyl group, aryl group, alkoxy group and amino group.

[0066] Each of the group of atoms [—C(=L¹)-(E)_(x)-C(═X¹)—] (hereinafter referred to as “W1”) connecting to Y¹ and the group of atoms [—C(=L⁵)—(G)_(y)-C(═X²⁻)—] (hereinafter referred to as “W2”) connecting to Z¹ forms a conjugated system, and therefore each of the carbon ring or heterocyclic, ring constituting W1 and Y¹ and that of W2 and Z¹ has a resonating structure.

[0067] Each of the carbon ring or heterocyclic ring of W1 and Yl and that of W2 and Z¹ is preferably a 4- to 7-membered ring, more preferably a 5- or 6-membered ring. Each ring may form a condensed-ring with other 4- to 7-membered rind and may have substituent groups. Examples of the substituent groups are the same as those described hereinbefore for A¹, A², B¹ and B². Examples of preferred hetero-atoms in the heterocyclic ring include B. N, O, S, Se and Te. Among them, N, O and S are particularly preferred.

[0068] Each of the numbers represented by x and y is independently 0 or 1, and preferably both of them are 0.

[0069] X¹ is ═O, ═NR or ═C(CN)₂, and X² is —O, —NR or —C(CN)₂ in which R is a substituent group. Examples of the substituent group R are the same as those described hereinbefore for A¹, A², B¹ and B². Preferred substituent group R is an aryl group, and more preferably phenyl group. Preferred X¹ is ═O and preferred X² is —O.

[0070] Examples of the carbon ring constituting the set of W1 and Y¹ or the set of W2 and Z¹ include following rings (in which each of Ra and Rb independently represents hydrogen atom or a substituent group):

[0071] Among the above rings, A-1 and A-2 are preferred.

[0072] Examples of the heterocyclic rings consisting of the set of W1 and Y¹ or the set of W2 and Z¹ include following rings (in which each of Ra, Rb and Rc independently represents hydrogen atom or a substituent group):

[0073] Among the above heterocyclic rings, A-5, A-6 and A-7 are preferred. Each of Ra, Rb and Rc has the same meaning as that described hereinbefore for A¹, A² ₁, B¹ and B². Ra, Rb and Rc may be combined to from a saturated or unsaturated carbon ring (e.g., cyclohexyl ring, cyclopentyl ring, cyclohexene ring, and benzene ring), or a saturated or unsaturated heterocyclic ring (e.g., piperidine ring, piperazine ring, morpholino ring, tetrahydrofuran ring, furan ring, thiophene ring, pyridine ring, and pyrazine ring). In that case, the ring may have one or more substituent groups. Examples of the substituent groups are the same as those described hereinbefore for A¹, A², B¹ and B².

[0074] Each of L¹, L², L³, L⁴ and L⁵ independently represents a methine group which may have one or more substituent groups. Examples of the substituent groups are the same as those described hereinbefore for A¹, A², B¹ and B². Among them, preferred substituent groups are an alkyl group, an aralkyl group, an aryl group, alkoxy group, an aryloxy group, an alkylthio group, an arylthio group, a halogen atom, an amino group, a carbamoyl group and a heterocyclic group. The substituent groups may be combined to form a 5- to 7-membered ring (e.g., cyclopentene ring, 1-dimethylaminocyclopentene ring, 1-diphenylaminocyclopentene ring, cyclohexene ring, 1-chlorocyclohexene ring, isophorone ring, 1-morpholinocyclopentene ring and cycloheptene ring).

[0075] Preferred combinations of integers of m and n are m=1 and n=1; m=0 and n=2; and m=2 and n=0.

[0076] Next, the cation part is described in detail.

[0077] The onium ion represented by M^(k+) comprises an onium atom which has positive charge and which has no hydrogen atoms thereon. Examples of the onium ions include a quaternary ammonium ion, oxonium ion, sulfonium ion, phosphonium ion, selenonium ion, and iodonium ion. Preferably, M^(k+) is not a cyanine dye but a quaternary ammonium ion.

[0078] A quaternary ammonium can be obtained by alkylation (Menshutkin reaction), alkenylation, alkynylation or arylation of a tertiary amine (e.g., trimethylamine, triethylamine, tributylamine, triethanolamine, N-methylpyrrolidine, N,N-dimethylpiperazine, triethylenediamine, and N,N,N′,N′-tetramethylethylenediamine) or a nitrogen-containing heterocyclic ring (pyridine, picoline, 2,2′-bipyridyl, 4,4′-bipyridyl, 1,10-phenanthroline, quinoline, oxazole, thizole, N-methylimidazole, pyrazine, and tetrazole).

[0079] M^(k+) preferably is a quaternary ammonium ion comprising a nitrogen-containing heterocyclic ring, and more preferably a quaternary pyridinium ion,

[0080] k is an integer of 1 to 10, preferably 1 to 4. More preferably, k is 2.

[0081] The most preferred onium ions for M^(k+) are ionic compounds having the below-mentioned formula (II) or (III):

[0082] in which each of R¹, R², R⁵ and R⁶ independently represents an alkyl group, an alkenyl group, an alkynyl group, an, aryl group or a heterocyclic group; each of R³, R⁴, R⁷ and R⁸ independently represents a substituent group (including substituent atom); or each set of R³ and R⁴, R⁵ and R⁶, R⁷ and R⁸, R¹ and R³, R² and R⁴, R⁵ and R⁷ or R⁶ and R⁸ can be combined to form a ring; each of q1, q2, r1 and r2 independently represents an integer of 0 to 4; under the condition that there can be different R³, R⁴, R⁷ and R⁸ in the case that q1, q2, r1 and r2 are 2 or more.

[0083] The above-mentioned onium ion for M^(k+) can be obtained by Menshutkin reaction (described in, for instance, Japanese Patent Provisional Publication 61-148162) or arylation (described in, for instance, Japanese Patent Provisional Publications 51-16675 and H1-96171) of 2,21-bipyridyl or 4,4′-bipyridyl with a halide having the desired substituent.

[0084] The alkyl group preferably used for R¹, R², R⁵ and R⁶ is an alkyl group of 1-18 carbon atoms which may have one or more substituent groups, and more preferably an alkyl group of 1-8 carbon atoms which may have one or more substituent groups. Examples of the alkyl groups include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, n-hexyl, cyclohexyl and cyclopropyl.

[0085] Examples of substituent groups for the alkyl groups include:

[0086] a halogen atom (e.g., fluorine, chlorine, and bromine);

[0087] an alkoxy group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methoxy and ethoxy);

[0088] an aryloxy group of 6-10 carbon atoms which may have one or more substituent groups (e.g., phenoxy and p-methoxyphenoxy);

[0089] an alkylthio group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methylthio and ethylthio);

[0090] an arylthio group of 6-10 carbon atoms which may have one or more substituent groups (e.g., phenylthio);

[0091] an acyl group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., acetyl and propionyl);

[0092] an alkylsulfonyl or arylsulfonyl group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., methanesulfonyl and p-toluenesulfonyl);

[0093] an acyloxy group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., acetoxy and propionyloxy);

[0094] an alkoxycarbonyl group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., methoxycarbonyl and ethoxycarbonyl);

[0095] an alkenyl group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., vinyl);

[0096] an alkynyl group of 2-18 (preferably 2-8) carbon atoms which may have one or more substituent groups (e.g., ethynyl);

[0097] an aryl group of 6-10 carbon atoms which may have one or more substituent groups (e.g., phenyl and naphthyl);

[0098] an aryloxycarbonyl group of 7-11 carbon atoms which may have one or more substituent groups (e.g., naphthoxycarbonyl);

[0099] an amino group having 0-18 (preferably 0-8) carbon atoms which may have one or more substituent groups (e.g., un-substituted amino, methylamino, dimethylamino, diethylamino, anilino, methoxyphenylamino, chlorophenylamino, morpholino, piperidino, pyrrolidino, pyridylamino, methoxycarbonylamino, n-butoxycarbonylamino, phenoxycarbonylamino, methylcarbamoylamino, ethylthiocarbamoylamino, phenylcarbamoylamino, acetylamino, ethylcarbonylamino, ethylthiocarbonylamino, cyclohexylcarbonylamino, benzoylamino, chloroacetylamino, and methylsulfonylamino);

[0100] a carbamoyl group of 1-18 (preferably 1-8) carbon atoms which may have one or more substituent groups (e.g., non-substituted carbamoyl, methylcarbamoyl, ethylcarbamoyl, n-butylcarbamoyl, t-butylcarbamoyl, dimethylcarbamoyl, morpholinocarbamoyl, and pyrrolidinocarbamoyl);

[0101] a sulfamoyl group having 0-18 (preferably 0-8) carbon atoms which may have one or more substituent groups (e.g., non-substituted sulfamoyl, methylsulfamoyl, and phenylsulfamoyl);

[0102] cyano group; nitro group; carboxyl group; hydroxyl group; and

[0103] a heterocyclic group (e.g., oxazole, benzoxazole, thiazole, benzothiazole, imidazole, benzoimidazole, indolenine, pyridine, sulfolane, furan, thiophene, pyrazol, pyrrole, chroman, and coumarin).

[0104] The alkenyl group for R¹, R², R¹ and R⁶ preferably is an alkenyl group of 2-18 carbon atoms which may have one or more substituent groups, and more preferably an alkenyl group of 2-8 carbon atoms which may have one or more substituent groups. Examples of the alkenyl groups include vinyl, allyl, 1-propenyl and 1,3-butadienyl.

[0105] Examples of substituent groups for the alkenyl groups are the same as those described hereinbefore for alkyl group.

[0106] The alkynyl group for R¹, R², R⁵ and R⁶ preferably is an alkynyl group of 2-18 carbon atoms which may have one or more substituent groups, and more preferably an alkynyl group of 2-8 carbon atoms which may have one or more substituent groups. Examples of such alkynyl group include ethynyl and 2-propynyl.

[0107] Examples of substituent groups for the alkynyl groups are the same as those described hereinbefore for alkyl group.

[0108] The aryl group for R¹, R², R⁵ and R⁶ preferably is an aryl group of 6-18 carbon atoms which may have one or more substituent groups. Examples of such aryl group include phenyl and naphthyl.

[0109] Examples of substituent groups for the aryl groups are the same as those described hereinbefore for alkyl group. Alkyl groups (e.g., methyl and ethyl) are also preferably used as the substituent groups.

[0110] Examples of the heterocyclic groups preferably employable for R¹, R², R⁵ and R⁶ include oxazole, benzoxazole, thiazole, benzothiazole, imidazole, benzoimidazole, indolenine, pyridine, sulfolane, furan, thiophene, pyrazol, pyrrole, chroman and coumarin.

[0111] Each of R³, R⁴, R⁷ and R¹ has the same meaning as that described hereinbefore for A¹, A², B¹ and B² Examples of the preferred substituent groups of R³, R⁴, R⁷ and R⁸ include a hydrogen atom and an alkyl group. Among them, a hydrogen atom is particularly preferred.

[0112] R⁵ and R⁶ are preferably combined to form a ring. In such case, the ring preferably has 5 to 7 members, more preferably 6 members. Each of a set of R³ and R⁴ and a set of R⁷ and R⁸ is preferably combined to form a carbon ring or a heterocyclic ring, more preferably a carbon ring. It is particularly preferred that each of the sets be combined with the connected pyridine ring to form a condensed aromatic ring.

[0113] In the oxonol compounds of the formulas (IV-1) and (IV-2), A³, A⁴, B³ and B⁴; Y² and Z²; L⁶ L⁷ L⁸ L⁹ and L¹⁰ and m1 and n1 have the same meaning as those of A¹, A², B¹ and B²; Y¹ and Z¹; L¹, L², L³, L⁴ and L⁵; and m and n in the formulas (IV-1) and (IV-2), respectively. Consequently, preferred examples of them are the same.

[0114] In M²⁺ of the formulas (V) and (VI), R¹¹, R¹², R¹³, R¹⁴, R¹⁵, R¹⁶ R¹⁷ and R¹⁸; and q3, r3, q4 and r4 have the same meaning as those of R¹, R², R³, R⁴, R⁵, R⁶, R⁷ and R⁸; and q1, r1, q2 and r2 in the formulas (II) and (III), respectively. Consequently, preferred examples of them are the same.

[0115] Concrete examples of preferred anion parts of the dye compounds of the formulas (I-1) and (I-2) are given below.

No. Ra Rb B-1 COOEt H B-2 COOEt CH₃ B-3 COOEt Ph B-4 COOEt CH₂CH₂OH B-5 COOCH₃ Ph B-6 COOEt

B-7 COOEt CONHC₄H₉ ^((n)) B-8 COOEt CONHPh B-9 CN Ph B-10 COCH₃ Ph B-11 CF₃ Ph B-12 CONHCH₃ CH₃ B-13 CONHCH₃ Ph B-14 CONHC₄H₉ ^((n)) Ph B-15 CONHPh Ph B-16 CONHCH₃

[0116]

No. Ra Rb L B-17 CONHC₄H₉ ^((n)) CONHC₄H₉ ^((n)) CH B-18 Ph H CH B-19 Ph CH₃ CH B-20 Ph Ph CH B-21 Ph

CH B-22

Ph CH B-23

Ph CH B-24

Ph CH B-25 Ph

C(CH₃) B-26 Ph CONHC₄H₉ ^((n)) CH B-27 Ph

CH B-28 COOEt CH₂Ph CH B-29 SO₂CH₃ Ph CH

[0117]

No. Ra Rb L n B-30 CH₃SO₂NH Ph CH 1 B-31 HO Ph C(CONH₂) 1 B-32 CH₃ Ph C(Ph) 1 B-33 CH₃ Ph C(CH₂Ph) 1 B-34 CH₃ Ph

1 B-35 EtO Ph CH 1 B-36 NHCOCH₃ Ph CH 1 B-37 NHCOPh Ph CH 1 B-38 NHCOPh CONHC₄H₉ ^((n)) CH 1 B-39 NHCOPh CONHPh CH 1 B-40 COOEt

CH 0 B-41 CN

CH 0 B-42 CF₃ Ph CH 0 B-43 CONHC₄H₉ ^((n)) Ph CH 0 B-44 NHCOC₄H₉ ^((n)) Ph CH 0

[0118]

No. Ra Rb L B-45

CH B-46 NH₂ Ph CH B-47 NHCONHC₄H₉ ^((n)) Ph CH B-48 NHCOOC₄H₉ ^((n)) Ph CH B-49

CH₂Ph CH B-50 NHCOPh Ph C(Ph) B-51

Ph CH B-52

CH B-53 CN

CH B-54 CF₃

CH

[0119]

No. Ra Rb L B-55 COOEt

C(CH₃) B-56 CN

C(CH₃) B-57 CF₃

C(CH₃) B-58 COCH₃

C(CH₃) B-59 COOEt

C(CH₃) B-60 CN

C(CH₃) B-61 COOEt

C(Br) B-62 COOEt

C(Cl) B-63 CN

C(Br)

[0120]

No. Ra Rb L B-64 CN Ph C(Br) B-65 COOEt Ph C(Cl) B-66 COOEt Ph CH B-67 CONHCH₃ Ph CH B-68 NHCOCH₃ Ph CH B-69 CH₃ Ph CH B-70 NH₂ Ph CH

[0121]

No. Ra Rb X L B-71 H H O CH B-72 H CH₃ O CH B-73 H n-C₄H₉ O CH B-74 n-C₄H₉ n-C₄H₉ O CH B-75 H Ph O CH B-76 H Ph O C(Ph) B-77 Ph Ph O CH B-78 H

O CH B-79 H

O CH B-80 H H S CH B-81 H C₂H₅ S CH B-82 C₂H₅ C₂H₅ S CH B-83 H n-C₄H₉ O C(CH₂Ph) B-84 H Ph O C(CH₃) B-85 H Ph S CH

[0122]

No. Ra Rb X L B-86 H n-C₄H₉ O CH B-87 H Ph O CH B-88 CH₃ CH₃ O CH B-89 Ph Ph O CH B-90 H Ph O C(CH₃) B-91 H

O C(CH₂Ph) B-92 H n-C₄H₉ S CH B-93 H Ph S CH B-94 Ph Ph S CH B-95 Et Et S CH B-96 H Ph S C(CH₃)

[0123]

[0124] Concrete examples of preferred cation parts of the dye compounds of the formulas (I-1) and (I-2) are given below.

No. R¹ R² C-17 CH₃ CH₃ C-18 C₂H₅ C₂H₅ C-19 n-C₃H₇ n-C₃H₇ C-20 n-C₄H₉ n-C₄H₉ C-21 iso-C₄H₉ iso-C₄H₉ C-22 n-C₆H₁₃ n-C₆H₁₃ C-23 PhCH₂ PhCH₂ C-24 CH₃—CH═CH—CH₂ CH₃—CH═CH—CH₂ C-25 CH₂═CH CH₂═CH C-26 NCCH₂ NCCH₂ C-27 EtO₂C—CH₂ EtO₂C—CH₂ C-28 HOCH₂CH₂ HOCH₂CH₂ C-29 EtOCH₂CH₂ EtOCH₂CH₂ C-30 CH₃ n-C₄H₉ C-31 CH₃ PhCH₂ C-32 CH₃COCH₂ CH₃COCH₂ C-33

C-34 CF₃CH₂ CF₃CH₂ C-35 Ph Ph C-36

C-37

C-38

C-39

C-40

C-41

C-42

C-43

C-44

C-45

C-46

C-47

C-48

C-49

C-50

C-51

C-52

C-53

C-54

C-55

C-56

C-57

C-58

C-59

C-60

C-61

C-62

C-63

C-64

C-65

C-66

C-67

C-68

C-69

C-70

C-71

C-72

C-73

C-74

C-75

C-76

C-77

C-78

C-79

C-80

C-81

C-82

C-83

C-84

C-85

C-86

C-87

C-88

[0125] Concrete examples of the compounds preferably employable for the invention are set forth in Table 1. In Table 1, each compound is shown as a combination of the anion part and the cation part. For example, the compound of No. 1 (Compound No. 1) consists of the anion part of (B-3) and the cation part of (C-1), and the compound of No. 5 (Compound No. 5) consists of the anion part of (B-3) and the cation part of (C-22). Consequently, each of the compounds of No. 1 and No. 5 has the below-mentioned formula:

[0126] The compounds in Table 1 can be illustrated in the same manner as those of No. 1 and No. 5 described above. TABLE 1 Compound anion cation No. 1 B-3 C-1 No. 2 B-3 C-3 No. 3 B-3 C-8 No. 4 B-3 C-17 No. 5 B-3 C-22 No. 6 B-3 C-41 No. 7 B-3 C-46 No. 8 B-3 C-51 No. 9 B-3 C-53 No.10 B-6 C-1 No.11 B-6 C-3 No.12 B-6 C-8 No.13 B-6 C-17 No.14 B-6 C-22 No.15 B-6 C-41 No.16 B-6 C-46 No.17 B-6 C-51 No.18 B-6 C-53 No.19 B-9 C-51 No.20 B-11 C-51 No.21 B-20 C-1 No.22 B-20 C-3 No.23 B-20 C-8 No.24 B-20 C-17 No.25 B-20 C-22 No.26 B-20 C-41 No.27 B-20 C-46 No.28 B-20 C-51 No.29 B-20 C-53 No.30 B-21 C-51 No.31 B-25 C-51 No.32 B-27 C-51 No.33 B-40 C-1 No.34 B-40 C-8 No.35 B-40 C-51 No.36 B-40 C-53 No.37 B-41 C-20 No.38 B-41 C-51 No.39 B-41 C-53 No.40 B-42 C-51 No.41 B-53 C-3 No.42 B-53 C-8 No.43 B-53 C-17 No.44 B-53 C-22 No.45 B-53 C-51 No.46 B-55 C-51 No.47 B-61 C-22 No.48 B-61 C-51 No.49 B-61 C-53 No.50 B-62 C-51 No.51 B-64 C-51 No.52 B-71 C-1 No.53 B-71 C-3 No.54 B-71 C-8 No.55 B-71 C-17 No.56 B-71 C-22 No.57 B-71 C-41 No.58 B-71 C-46 No.59 B-71 C-51 No.60 B-71 C-53 No.61 B-75 C-3 No.62 B-75 C-8 No.63 B-75 C-35 No.64 B-75 C-51 No.65 B-75 C-53 No.66 B-76 C-30 No.67 B-76 C-51 No.68 B-78 C-1 No.69 B-78 C-51 No.70 B-82 C-3 No.71 B-82 C-51 No.72 B-83 C-3 No.73 B-83 C-4 No.74 B-83 C-8 No.75 B-83 C-21 No.76 B-83 C-30 No.77 B-83 C-46 No.78 B-83 C-51 No.79 B-83 C-58 No.80 B-87 C-3 No.81 B-87 C-30 No.82 B-87 C-51 No.83 B-93 C-3 No.84 B-93 C-30 No.85 B-93 C-51 No.86 B-97 C-51 No.87 B-97 C-53 No.88 B-99 C-51 No.89 B-99 C-53 No.90 B-107 C-3 No.91 B-107 C-22 No.92 B-107 C-41 No.93 B-107 C-46 No.94 B-107 C-51 No.95 B-115 C-51 No.96 B-126 C-51 No.97 B-134 C-51 No.98 B-138 C-51 No.99 B-152 C-3 No.100 B-152 C-51 No.101 B-155 C-3 No.102 B-155 C-51 No.103 B-161 C-3 No.104 B-161 C-51 No.105 B-3 C-73 No.106 B-21 C-76 No.107 B-82 C-74 No.108 B-82 C-84 No.109 B-115 C-74 No.110 B-162 C-22 No.111 B-162 C-74 No.112 B-162 C-77 No.113 B-164 C-77 No.114 B-166 C-76 No.115 B-167 C-77 No.116 B-186 C-73 No.117 B-188 C-73 No.118 B-192 C-77 No.119 B-196 C-77 No.120 B-198 C-77 No.121 B-199 C-77 No.122 B-75 C-85 No.123 B-75 C-86 No.124 B-75 C-87

[0127] The compound represented by the formula (1-1) or (1-2) can be easily prepared by an ion-exchange reaction between the onium salt having the below-mentioned formula VIII) and a salt of the dye compound having the below-mentioned formula (VII-1) or (VII-2). The dye compound can be used in the form of an alkaline metal salt (e.g., Li salt, Na salt, and K salt), an ammonium salt (NH₄ ⁺ salt) or a salt having an organic counter ion such as a triethylammonium salt (Et₃NH⁺ salt) or a tributylammonium salt (Bu₃NH⁺ salt). The ion-exchange reaction can be carried out in water or in an organic solvent (e.g., methanol, ethanol, isopropanol, and dimethylformamide).

[0128] In the above formulas, A⁵, A⁶, B⁵ and B⁶; Y³ and Z³; L¹¹, L¹², L¹³, L¹⁴ and L¹⁵; X³ and X⁴; E1 and G1; m3 and n3; and x1 and y1 are the same meaning as A¹, A², B¹ and B²; y, and Z¹; L¹, L², L³, L⁴ and Ls; X¹ and X²; E and G; m and n; and x and y in the formulas (I-1) and (I-2), and X^(r−) in the formula (VII) represents an anion, and r represents an integer of not less than 1 (preferably 1 to 4, more preferably 1 or 2). Examples of the anions include halide ions (e.g., Cl⁻, Br⁻, and I⁻), sulfonato ions (CH₃SO₃ ⁻, p-toluenesulfonato ion, and naphthalene-1,5-disulfonato ion), ClO₄ ⁻, BF₄ ⁻, and PF₆ ^(−.)

[0129] The dye compound represented by the formula (VII-1) or (VII-2) can be prepared by a condensation reaction between the corresponding active methylene compound (e.g., pyrazolone, thiobarbituric acid, barbituric acid, indandione, and hydroxyphenalenone) and the methine source to introduce a methine group or polymethine group into the methine dye. The methine source are described in detail in Japanese Patent Publication Nos. 39-22069, 43-3504, 52-38056, 54-38129, 55-10059, 58-35544; Japanese Patent Provisional Publication Nos. 49-99620, 52-92716, 59-16834, 63-316853, 64-40827; British Patent No. 1133986; U.S. Pat. Nos. 3,247,127, 4,042,397, 4,181,225, 5,213,956 and 5,260,179. Concrete examples of the methine source for introducing of monomethine group include ortho esters (e.g., ethyl orthoformate and ethyl orthoacetate) and N,N-diphenylformamidine hydrochloride. Examples of the methine source for introducing of trimethine chain include trimethoxypropane, 1,1,3,3-tetramethoxypropane and malonaldehydodianyl hydrochloride (and the derivatives of those above described). Examples of the methine source for introducing of pentamethine chain include glutaconaldehydodianyl hydrochloride and 1-(2,4-dinitrophenyl)pyridiniumchloride (and the derivatives of those above described).

[0130] The syntheses of the dye compounds represented by the formula (I-1) or (I-2) are described below.

SYNTHESIS EXAMPLES Synthesis Example 1 Synthesis of Compound No. 5

[0131] 1 g of the compound (a) having the below-illustrated formula was added to 20 ml of 0.1 N aqueous NaOH solution, and stirred at room temperature. Independently, 0.5 g of the compound (b) having the below-mentioned formula was dissolved in 5 ml of water. The prepared solutions were mixed and stirred at room temperature for 30 minutes, and then the formed precipitate was collected by filtration. The obtained precipitate was washed successively with water and ethanol, and then dried to give 0.23 g of the desired compound. λ_(max)=654 nm (in methanol)

Synthesis Example 2 Synthesis of Compound No. 8

[0132] 0.53 g of the above compound (a) was added to 10 ml of 0.1 N aqueous NaOH solution, and stirred at room temperature. Independently, 0.2 g of the compound (c) having the below-mentioned formula was dissolved in 5 ml of water. The prepared solutions were mixed and stirred at room temperature for 30 minutes, and then the formed precipitate was collected by filtration. The obtained precipitate was washed successively with water and ethanol, and then dried to prepare 0.4 g of the desired compound. λ_(max)=654 nm (in methanol)

Synthesis Example 3 Synthesis of Compound No. 9

[0133] 1 g of the above compound (a) was suspended in 20 ml of water. To the prepared suspension, 20 ml of 0.1 N aqueous NaOH solution was added and stirred at room temperature. Independently, 0.4 g of the compound (d) having the below-mentioned formula was dissolved in 5 ml of water. The prepared liquids were mixed and stirred at room temperature for 30 minutes, and then the formed precipitate was collected by filtration. The obtained precipitate was washed with water and ethanol, and then dried to prepare 0.2 g of the desired compound. λ_(max)=654 nm (in methanol)

Synthesis Example 4 Synthesis of Compound No. 28

[0134] 1 g of the compound (e) having the below-mentioned formula was added in 10 ml of methanol. Into the prepared solution, 0.1 ml of 25 W aqueous NH₃ solution was dropped under stirring at room temperature. Independently, 0.5 g of the above compound (c) was dissolved in 2 ml of water. The prepared solutions were mixed and stirred at room temperature for 30 minutes, and then the formed precipitate was collected by filtration. The obtained precipitate was washed with methanol, and then dried to prepare 0.8 g of the desired compound. λ_(max)=637 nm (in methanol)

Synthesis Example 5 Synthesis of Compound No. 67

[0135] 0.55 g of the compound (f) having the below-mentioned formula was dissolved in 10 ml of DMF. To the prepared solution, 0.17 g of the above compound (c) was added and stirred at room temperature for 1 hour, and then 70 ml of water was added to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.5 g of the desired compound. λ_(max)=607 nm (in methanol):

Synthesis Example 6 Synthesis of Compound No. 71

[0136] 0.93 g of the compound g) having the below-mentioned formula was added in 30 ml of methanol. Independently, 0.35 g of the above compound (c) was dissolved in 20 ml of methanol. The prepared solutions were mixed and stirred at room temperature for 150 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.9 g of the aimed compound. λ_(max)=633 nm (in methanol)

Synthesis Example 7 Synthesis of Compound No. 86

[0137] 1.0 g of the compound (h) having the below-mentioned, formula was added in methanol, and then 0.35 ml of triethylamine was further added. To the solution, 0.46 g of the above compound (c) was added and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.85 g of the desired compound. λ_(max)=661 nm (in methanol)

Synthesis Example 8 Synthesis of Compound No. 89

[0138] 1.1 g of the compound (i) having the below-mentioned formula was added in 2.5 ml of 1 N aqueous NaOH solution. To the solution, 0.46 g of the above compound (d) was added and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.9 g of the desired compound. A=652 nm (in methanol)

Synthesis Examples 9-11

[0139] Synthesis of Compounds Nos. 45, 46 and 98

[0140] Compounds Nos. 45, 46 and 98 were synthesized in the same manner as in the Synthesis Example 2 or 4. The absorption spectrum of each prepared compound in methanol was observed to find the absorption maxim (λ_(max)) as follows:

[0141] Compound No. 45: λ_(max) located at 654 nm;

[0142] Compound No. 46: λ_(max) located at 674 nm; and

[0143] Compound No. 98: λ_(max) located at 603 nm.

Synthesis Example 12 Synthesis of Compound No. 1

[0144] 2.6 g of the above compound (a) was added in 50 ml of 0.1 N NaOH aqueous solution. To the solution, 0.8 g of tetramethylammoniumbromide was added and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration washed with water, and then dried to prepare 2.45 g of the desired compound. λ_(max)=654 nm (in methanol).

Synthesis Examples 13-15

[0145] Synthesis of Compounds Nos. 3, 6 and 7

[0146] The procedure of Synthesis Example 12 was repeated except that tetramethylammonium bromide was replaced with each corresponding quaternary ammonium bromide, to synthesize each of Compounds Nos. 3, 6 and 7, λ_(max)=654 nm (in methanol) for all

Synthesis Example 16 Synthesis of Compound No. 99

[0147] 1.3 g of the compound (j) having the below-mentioned formula was added in 10 ml of methanol. Into the prepared solution, 0.15 ml of 25% aqueous NH₃ solution was dropped under stirring at room temperature, and then 1.4 g of tetrabutylammonium bromide was added and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.2 g of the desired compound. λ_(max)=671 nm (in methanol)

Synthesis Example 17 Synthesis of Compound No. 100

[0148] 1.3 g of the above compound (j) was added in 10 ml of methanol. Into the prepared solution, 0.15 ml of 25% NH₃ aqueous solution was dropped under stirring at room temperature. Independently, 0.38 g of the above compound (c) was dissolved in 20 ml of methanol. The prepared solutions were mixed and stirred at room temperature for 120 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.7 g of the desired compound. λ_(max)=671 nm (in methanol)

Synthesis Example 18 Synthesis of Compound No. 102

[0149] The procedure of Synthesis Example 17 was repeated except that the compound (j) was replaced with 1.1 g of the compound (x) having the below-mentioned formula, to prepare 0.45 g of Compound No. 102, n=655 nm (in methanol)

Synthesis Example 19 Synthesis of Compound No. 106

[0150] 1.0 g of the compound (1) having the below-mentioned formula was added in 10 ml of methanol, and then 0.2 ml of triethylamine was further added. Independently, 0.3 g of the compound (m) having the below-mentioned formula was dissolved in 10 ml of methanol. The prepared solutions were mixed and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.6 g of the desired compound. λ_(max)=636 nm (in methanol)

Synthesis Example 20 Synthesis of Compound No. 107

[0151] 1.6 g of the aforementioned compound (g) was added in 20 ml of methanol, and then 0.5 ml of triethylamine was further added. Independently, 1 g of the compound (n) having the below-mentioned formula was dissolved in 5 ml of methanol. The prepared solutions were mixed and stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 1.6 g of the desired compound. λ_(max)=640 nm (in DMF).

Synthesis Example 21 Synthesis of Compound No. 109

[0152] 2.5 g of the compound (o) having the below-mentioned formula was added in 50 ml of DMF, and then 1 ml of triethylamine was further added. Independently, 1.5 g of the compound (n) was dissolved in 5 ml of methanol. The prepared solutions were mixed and then 50 ml of methanol was dropwise added. The solution was stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 3 g of the desired compound. λ_(max)=707 nm (in methanol)

Synthesis Example 22 Synthesis of Compound No. 112

[0153] 3.5 g of the compound (p) having the below-mentioned formula was added in 50 ml of methanol, and then 1.5 ml of triethylamine was further added. Independently, 2.5 g of the compound (q) having the below-mentioned formula was dissolved in 10 ml of methanol. The prepared solutions were mixed to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 4.4 g of the desired compound. λ_(max)=661 nm (in DMF).

Synthesis Example 23 Synthesis of Compound No. 115

[0154] The procedure of Synthesis Example 22 was repeated except that the compound (p) was replaced with 4.6 g of the compound (r) having the below-mentioned formula, to synthesize 2.3 g of Compound No. 115. λ_(max)=655 nm (in methanol)

Synthesis Example 24 Synthesis of Compound No. 116

[0155] 0.3 g of the compound (s) having the following formula was added to the mixed solvent of 5 ml of DMF and 15 ml of methanol, and then 1.2 ml of tributylamine was dropwise added under stirring. The resulting solution was, further stirred for 30 minutes at room temperature, and then 0.3 g of the compound (t) having the below-mentioned formula was added. The solution was kept stirring for 2 hours to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.25 g of the desired compound. λ_(max)=606 nm (in DMF).

Synthesis Example 25 Synthesis of Compound No. 117

[0156] 0.23 g of the compound (u) having the following formula was added in methanol, and then 1.2 ml of tributylamine was further added. To the resulting solution, 0.28 g of the above compound (t) was added. The resulting solution was stirred at room temperature for 60 minutes to form precipitate. The precipitate was collected by filtration and washed with methanol, and then dried to prepare 0.22 g of the desired compound. λ_(max)=609 nm (in DMF).

[0157] Each of the compounds of the formula (I-1) or (I-2) of the invention can be employed singly or in combination with two or more compounds. Further, a combination of plural compounds having the formula (I-1) and a combination of plural compounds having the formula (I-2) can be also employed. Furthermore, the compound of the invention can be also employed in combination with other known compounds.

[0158] The information recording medium of the invention has a recording layer provided on a support, in which the recording layer contains the dye compound represented by the formula (I-1) and/or (I-2). The information recording medium of the invention preferably has a light-reflecting layer provided on the recording layer, and preferably has the medium also has a protective layer provided on the light-reflecting layer.

[0159] The information recording medium of the invention can be prepared by the following method.

[0160] The substrate (support) which is transparent can be made of any of materials known as the materials for the producing the substrate of the light information recording medium. Examples of the materials include glass, polycarbonate, acrylic resins such as polymethyl methacrylate, vinyl chloride resins such as polyvinyl chloride and vinyl chloride copolymer, epoxy resins, amorphous polyolefins, and polyesters. These materials can be employed in combination, if desired. These materials are molded to give a film or a rigid plate. Most preferred is a polycarbonate resin from the viewpoints of anti-humidity and dimensional stability.

[0161] The substrate may have on its surface on the recording layer side an undercoating layer for enhancing surface smoothness and adhesion, and keeping the dye recording layer from deterioration. Examples of the material for the undercoating layer include polymers such as polymethyl methacrylate, acrylate-methacrylate copolymer, styrene-maleic anhydride copolymer, polyvinyl alcohol, N methylolacrylamide, styrene-vinyltoluene copolymer, chlorosulfonated polyethylene, nitrocellulose, polyvinyl chloride, chlorinated polyolefin, polyester, polyimide, vinyl acetate-vinyl chloride copolymer, ethylene-vinyl acetate copolymer, polyethylene, polypropylene, and polycarbonate, and surface treating agents such as a silane-coupling agent.

[0162] The undercoating layer can be formed by coating a solution in which one or more of the above-mentioned materials are dissolved or dispersed on the surface of the substrate by the known coating methods such as spin-coat, dip-coat, and extrusion-coat. The undercoating layer generally has a thickness of 0.005 to 20 μm, preferably 0.01 to 10 μm.

[0163] On the surface of the substrate or on the undercoating layer, groove for tracking or giving address signals is preferably formed. The groove is preferably formed directly on the surface of the substrate when the substrate is molded from polymer material by injection or extrusion.

[0164] Alternatively, the groove can be provided on the surface of the substrate by placing a pregroove layer. The pregroove layer can be produced from a mixture of a monomer such as monoester, diester, triester, or tetraester of acrylic acid, or its oligomer, and a light-polymerization reaction initiator. The pregroove layer can be produced by the steps of coating a mixture of the polymerization initiator and the monomer such as the above-mentioned acrylic ester on a precisely produced stamper, placing on the coated layer a substrate, and irradiating the coated layer with ultra-violet rays through the stamper or substrate, so as to cure the coated layer as well as to combine the cured layer and the substrate. The substrate to which the cured coated layer is attached is separated from the stamper, to give the desired substrate equipped with the pregroove layer. The thickness of the pregroove layer generally is in the range of 0.05 to 100 μm, preferably in the range of 0.1 to 50 μm.

[0165] The pregroove formed on the substrate preferably has a depth in the range of 300 to 2,000 angstroms and a half-width of 0.2 to 0.9 μm. The depth of 1,500 to 2,000 angstroms of the pregroove is preferably adopted because such pregroove can enhance the sensitivity without decreasing the light-reflection on the substrate. The optical disc having a recording layer (containing the dye compound of the formula (I-1) or (I-2)) coated on the deep pregoove and a light-reflection layer shows a high sensitivity, and hence is employable even in a recording system using a laser light of low laser power. This means that a semiconductor laser of a low coat can be employed or the life of semiconductor laser can be prolonged.

[0166] On the substrate, optionally via the undercoating, the recording layer containing the above-described dye compound of the invention is placed.

[0167] In order to improve light-resistance, the recording layer may contain various compounds known as singlet oxygen quencher. Examples of such compounds include a metal complex represented by the formula (III), (IV) or (V) of Japanese Patent Provisional Publication No. H3-224793; diimmonium salt; aminium salt; and nitroso compounds described in Japanese Patent Provisional Publications Nos. H2-300287 and H2-300288.

[0168] The recording layer can be formed on the substrate (support) by coating a solution of a mixture of the dye of the invention, and if desired, quencher and binder in an organic solvent and drying the coated layer. Examples of the organic solvents include esters such as butyl acetate and cellosolve acetate; ketones such as methyl ethyl ketone, cyclohexanone and methyl isobutyl ketone; chlorinated hydrocarbons such as dichloromethane, 1,2-dichloroethane and chloroform; amides such as dimethylformamide; hydrocarbons such as cyclohexanone; ethers such as tetrahydrofuran, diethyl ether and dioxane; alcohols such as ethanol, n-propanol, isopropanol, n-butanol, and diacetone alcohol; fluorine-containing solvents such as 2,2,3,3-tetrafluoropropanol; and glycol ethers such as ethyleneglycol monomethyl ether, ethyleneglycol monoethyl ether, and propyleneglycol monomethyl ether. These solvents can be employed in combination, in consideration of the solubility of the used compound in the solvent.

[0169] The coating solution can further contain auxiliary additives such as an oxidation inhibitor, a UV absorber, a plasticizer, and a lubricant.

[0170] Examples of the binders include natural-origin polymers such as gelatin, cellulose derivatives, dextran, rosin, and rubber; hydrocarbon polymer resins such as polyethylene, polypropylene, polystyrene and polyisobutyrene; vinyl polymers such as polyvinyl chloride, polyvinylidene chloride, and vinyl chloride-vinyl acetate copolymer; acrylate polymers such as polymethyl acrylate and polymethyl methacrylate; polyvinyl alcohol, chlorinated polyethylene; epoxy resins; butyral resins, rubber derivatives, and thermosetting resins such as prepolymers of phenol-formaldehyde. The binder is optionally employed in the amount of 0.01 to 50 weight parts, preferably 0.1 to 5 weight parts, per 1 weight part of the dye.

[0171] The coating solution generally has a concentration of 0.01 to 10 weight 0 (solid content), preferably 0.1 to weight W.

[0172] The coating can be performed by the known methods such as spray coat, spin coat, dip coat, roller coat, blade coat, doctor roller coat and screen print.

[0173] The recording layer can be a single layer or can comprise plural layers. The thickness of the recording layer generally is in the range of 20 to 500 nm, preferably 50 to 300 nm. The recording layer can be provided on both of the surfaces of the substrate.

[0174] On the recording layer, the light-reflecting layer is placed so as to enhance the light-reflection in the course of reproduction of information.

[0175] The light-reflecting material to be used for the formation of the light-reflecting layer should show a high reflection to the laser light. Examples of the light-reflecting materials include metals and submetals such as Mg, Se, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Re, Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt, Cu, Ag, Au, Zn, Cd, Al, Ga, In, Si, Ge, Te, Pb, Po, Sn, and Bi. Stainless steel film is also employable. Preferred light-reflecting material is Cr, Ni, Pt, Cu, Ag, Au and Al. These materials can be employed singly or in the form of alloy.

[0176] The light-reflecting layer can be formed on the recording layer by vacuum deposition, sputtering or ion-plating. The thickness of the light-reflecting layer generally is 10 to 200 nm, preferably 50 to 200 nm.

[0177] On the light-reflecting layer can be placed a protective layer. The protective layer can be placed on the substrate on the side not having the recording layer.

[0178] The protective layer can be formed of inorganic materials such as SiO, SiO₂, MgF₂, SnO₂, Si₃N₄; or organic materials such as thermo-plastic resins, thermo-setting resins, and UV curable resins.

[0179] The protective layer can be formed on the light-reflecting layer or the substrate by laminating a film of plastic material using an adhesive. The inorganic material can be placed on the light-reflecting layer or the substrate by vacuum deposition or spattering. The organic polymer material can be coated in the form of a solution containing the polymer material and dried to give the protective layer. The UV curable resin is dissolved in a solvent and coated on the light-reflecting layer or the substrate, and cured by applying ultra-violet rays to the coated layer. The coating layer can contain various additives such as an anti-static agent, an oxidation inhibitor, and a ultra-violet absorber. The protective layer generally has a thickness of 0.1 to 100 Am.

[0180] The information recording medium of the invention can comprise one substrate having one or two recording layers or two substrates each of which has one recording layer and combined to give a known air sandwich structure.

[0181] The information recording medium of the invention shows a high light-reflection and an improved light-resistance as well as good recording and reproducing characteristics. Particularly, the information recording medium of the invention shows an extremely high light-reflection of as high as 70%, and hence the reproduction of the recorded information can be accomplished by means of a commercially available CD player.

[0182] The information recording can be made in the following manner using the recording medium of the invention.

[0183] The information recording, medium is rotated at a predetermined constant line rate (1.2 to 14 m/sec., in the case of CD format) or a predetermined constant angle rate. On the rotated medium, a recording light source such as a semiconductor laser beam is applied through the transparent substrate. By the application of the laser beam, a pit is formed in the recording layer. The pit is assumed to be produced by local vacancy of the recording layer, deformation of the recording layer and/or the substrate, change of the physical or chemical characteristics of the recording layer. The light source preferably is a semiconductor layer having an oscillation frequency in the range of 500 to 850 nm. The preferred beam wavelength is in the range of 500 to 800 nm. In the case of the CR-R type recording medium, the laser beam preferably has a wavelength of 770 to 790 nm, while in the case of DVD-R type recording medium, the laser beam preferably has a wavelength of 630 to 680 nm.

[0184] The reproduction of the recorded information can be accomplished by applying a semiconductor laser beam on the medium rotated at the same rate as that employed in the recording procedure. The light-reflection is then detected on the substrate side.

[0185] The present invention is further described by the following non-restrictive working examples.

Example 1

[0186] 3 g of the oxonol dye compound (Compound No. 1) of the invention was dissolved in 100 ml of 2,2,3,3-tetrafluoropropanol to give a coating solution.

[0187] The coating solution was coated by spin coat on the surface of a polycarbonate substrate (diameter: 120 mm, thickness: 1.2 mm) to give a coated layer of approx. 200 nm thick. The substrate had a spirally formed pregroove (track pitch: 1.7 μm, groove width: 0.4 μm, depth: 0.16 μm) which was produced in the injection molding of the substrate.

[0188] On the coated dye layer was placed a light-reflecting layer of gold (thickness: approximately 100 nm) by sputtering, and then a UV curable photopolymer (UV curable agent: SD-220, available from Dainippon Ink & Chemicals, Inc.) was coated to give a coated layer of 7 μm thick. The coated layer was irradiated with ultra-violet rays to be cured to form a protective layer. Thus, an information recording disc according to the invention was prepared.

Examples 2-15

[0189] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of each of the compounds set forth in Table 2, to prepare information recording discs according to the invention.

Comparison Example 1

[0190] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of the following cyanine dye compound (Compound A) having the cation part of dye component and the anion part of perchlorate ion, to prepare an information recording disc for comparison.

Comparison Example 2

[0191] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of the following oxonol dye compound (Compound B) having an ammonium salt substituted with three ethyl groups in the cation part, to prepare an information recording disc for comparison:

Comparison Example 3

[0192] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of the following oxonol dye compound (Compound C) having an ammonium salt substituted with three ethyl groups in the cation part, to prepare an information recording disc for comparison.

Comparison Example 4

[0193] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of the following oxonol dye compound (Compound D) having an ammonium salt in the cation part, to prepare an information recording disc for comparison.

Comparison Example 5

[0194] The procedure of Example 1 was repeated except that the above oxonol dye compound (Compound No. 1) was replaced with the same amount of the following oxonol dye compound (Compound E) having an ammonium salt substituted with three ethyl groups in the cation part, to prepare an information recording disc for comparison.

[0195] [Evaluation of Information Recording Disc]

[0196] (1) Modulation

[0197] On the recording medium rotating at 1.4 m/sec., EFM signals of 3T and 11T were recorded by means of a laser beam of wavelength 780 nm. The laser power was varied in the range of 4 mW and 9 mW. The recorded signals were reproduced by the use of the laser beam having a laser power of 0.5 mW. The modulation factors of the 3T and 11T signals were measured under the optimum power.

[0198] (2) Light-Reflection

[0199] The light-reflections of the pregroove (non-recorded area) were also measured under the optimum power when the signals were reproduced.

[0200] (3) Light-Resistance

[0201] The recording medium was exposed to light from Xe lamp (140,000 lux) for 18 hours or for 36 hours. Thereafter, the modulation factors and pregroove light-reflections were measured in the same manner described above. At the same time, the color of the recording medium was observed by sight to classify the degree of fading into the following ranks: AA: not faded, BB: slightly faded but acceptable, and CC: completely faded.

[0202] The results are set forth in the following Table 2. TABLE 2 Oxonol Recording and Reproducing Characteristics Compound 3T Mod. 11T Mod. Reflection Fading (Example 1) Compound No. 1 (none) 0.402 0.701 72% — (18 hrs) 0.215 0.508 89% BB (36 hrs) - - - - - - - - - CC (Example 2) Compound No. 3 (none) 0.432 0.752 72% — (18 hrs) 0.253 0.520 88% BB (36 hrs) - - - - - - - - - CC (Example 3) Compound No. 5 (none) 0.423 0.753 68% — (18 hrs) 0.419 0.752 68% AA (36 hrs) 0.405 0.702 71% AA (Example 4) Compound No. 6 (none) 0.502 0.782 69% — (18 hrs) 0.495 0.752 69% AA (36 hrs) 0.295 0.552 76% BB (Example 5) Compound No. 7 (none) 0.498 0.778 69% — (18 hrs) 0.485 0.723 70% AA (36 hrs) 0.263 0.532 79% BB (Example 6) Compound No. 8 (none) 0.572 0.823 67% — (18 hrs) 0.572 0.823 67% AA (36 hrs) 0.571 0.821 67% AA (Example 7) Compound No. 9 (none) 0.512 0.767 68% — (18 hrs) 0.511 0.766 68% AA (36 hrs) 0.510 0.765 68% AA (Example 8) Compound No. 28 (none) 0.502 0.792 69% — (18 hrs) 0.502 0.791 69% AA (36 hrs) 0.501 0.790 69% AA (Example 9) Compound No. 45 (none) 0.552 0.803 69% — (18 hrs) 0.552 0.803 69% AA (36 hrs) 0.551 0.802 69% AA (Example 10) Compound No. 46 (none) 0.531 0.782 68% — (18 hrs) 0.530 0.782 68% AA (36 hrs) 0.528 0.781 69% AA (Example 11) Compound No. 67 (none) 0.522 0.773 68% — (18 hrs) 0.520 0.772 69% AA (36 hrs) 0.519 0.770 69% AA (Example 12) Compound No. 71 (none) 0.532 0.789 68% — (18 hrs) 0.531 0.788 68% AA (36 hrs) 0.529 0.785 69% AA (Example 13) Compound No. 86 (none) 0.547 0.798 69% — (18 hrs) 0.546 0.797 69% AA (36 hrs) 0.545 0.795 70% AA (Example 14) Compoun.d No. 89 (none) 0.562 0.813 70% — (18 hrs) 0.562 0.812 70% AA (36 hrs) 0.560 0.811 71% AA (Example 15) Compound No. 98 (none) 0.513 0.777 67% — (18 hrs) 0.502 0.722 69% AA (36 hrs) 0.415 0.542 73% AA (Example 16) Compound No. 99 (none) 0.502 0.745 70% — (18 hrs) 0.266 0.540 87% BB (36 hrs) - - - - - - - - - CC (Example 17) Compound No. 100 (none) 0.522 0.767 70% — (18 hrs) 0.519 0.765 71% AA (36 hrs) 0.516 0.763 73% AA (Example 18) Compound No. 102 (none) 0.512 0.753 72% — (18 hrs) 0.507 0.750 73% AA (36 hrs) 0.505 0.745 74% AA (Example 19) Compound No. 106 (none) 0.425 0.750 67% — (18 hrs) 0.420 0.749 67% AA (36 hrs) 0.407 0.700 70% AA (Example 20) Compound No. 107 (none) 0.530 0.786 68% — (18 hrs) 0.529 0.785 68% AA (36 hrs) 0.526 0.781 69% AA (Example 21) Compound No. 109 (none) 0.498 0.779 68% — (18 hrs) 0.497 0.778 68% AA (36 hrs) 0.495 0.777 69% AA (Example 22) Compound No. 112 (none) 0.512 0.767 70% — (18 hrs) 0.511 0.765 70% AA (36 hrs) 0.507 0.761 72% AA (Example 23) Compound No. 115 (none) 0.502 0.743 70% — (18 hrs) 0.502 0.722 71% AA (36 hrs) 0.497 0.719 72% AA (Example 24) Compound No. 116 (none) 0.518 0.773 67% — (18 hrs) 0.517 0.772 67% AA (36 hrs) 0.516 0.771 69% AA (Example 25) Compound No. 117 (none) 0.513 0.777 67% — (18 hrs) 0.512 0.776 67% AA (36 hrs) 0.510 0.774 68% AA (Example 26) Compound No. 119 (none) 0.470 0.763 69% — (18 hrs) 0.469 0.762 69% AA (36 hrs) 0.465 0.759 71% AA (Comparison Example 1) Compound A (none) 0.562 0.812 70% — (18 hrs) - - - - - - - - - CC (36 hrs) - - - - - - - - - CC (Comparison Example 2) Compound B (none) 0.395 0.698 66% — (18 hrs) - - - - - - - - - CC (36 hrs) - - - - - - - - - CC (Comparison Example 3) Compound C (none) 0.265 0.552 65% — (18 hrs) - - - - - - - - - CC (36 hrs) - - - - - - - - - CC (Comparison Example 4) Compound D (none) 0.355 0.652 65% — (18 hrs) - - - - - - - - - CC (36 hrs) - - - - - - - - - CC (Comparison Example 5) Compound E (none) 0.402 0.708 67% — (18 hrs) - - - - - - - - - CC (36 hrs) - - - - - - - - - CC

[0203] From the data set forth in Table 2, it is clear that each of the samples (Examples 1-18) of the invention (the information recording medium having the recording layer containing oxonol compound comprising a quaternary ammonium ion) gives relatively stable modulation factors even after exposure to light from Xe lamp, and therefore they have high light-resistance, as compared with the samples for comparison having the recording layer containing cyanine dye (Comparison Example 1), or oxonol compound comprising tertiary ammonium salt (Comparison Examples 2, 3 and 5) or ammonium salt (Comparison Example 4). In particular, the samples having the recording layer containing oxonol compound comprising divalent cation part (Examples 3-15, Examples 17-18) exhibit remarkably improved light-resistance. 

What is claimed is:
 1. An information recording medium comprising a support and a recording layer provided thereon on which information can be recorded by means of a laser beam; wherein said recording layer contains a dye compound having the following formula (I-1) or (I-2):

in which each of A¹, A², B¹ and B² independently represents a substituent group; each of Y¹ and Z¹ independently represents a group of atoms required for forming a carbon ring or a heterocydlic ring; each of E and G independently represents a group of atoms required for forming a conjugated double bond chain; X¹ represents ═O, ═NR or ═C(CN)₂, wherein R is a substituent group; X² represents —O, —NR or —C(N)₂₁ wherein R is a substituent group; each of L¹, L², L³, L⁴ and L⁵ independently represents a methine group which may have a substituent group; M^(k+) represents an onium ion containing a positively charged onium atom to which no hydrogen atom is attached; each of m and n independently is an integer of 0, 1 or 2; each of x and y, independently is an integer of 0 or 1; and x is an integer of 1 to
 10. 2. The information recording medium of claim 1, wherein M^(k+) is a quaternary ammonium ion.
 3. The information recording medium of claim 1, wherein k is
 2. 4. The information recording medium of claim 1, wherein M^(k+) is an onium ion having the following formula (II):

in which each of R¹ and R² independently represents a group selected from the group consisting of an alkyl group, an alkenyl group, an alkynyl group, an aryl group or a heterocyclic group; each of R³ and R⁴ independently represents a substituent group; or each set of R¹ and R³, R² and R⁴, or R³ and R⁴ can be combined to form a ring; each of q1 and r1 independently is an integer of 0 to 4; provided that plural R³ and plural R⁴ are the same as or different from each other in the case that q1 and r1 are 2 or more, respectively.
 5. The information recording medium of claim 1, wherein M^(k+) is an onium ion having the following formula (III):

in which each of R⁵ and R⁶ independently represents a group selected from the group consisting of an alkyl group, an alkenyl group, an alkynyl group, an aryl group and a heterocyclic group; each of R⁷ and R⁸ independently represents a substituent group; or each set of R⁵ and R⁶, R⁵ and R⁷, R⁶ and R¹, or R⁷ and R⁸ can be combined to form a ring; each of q2 and r2 independently is an integer of 0 to 4, provided that plural. R⁷ and plural R⁸ are the same as or different from each other in the case that q2 and r2 are 2 or more, respectively.
 6. The information recording medium of claim 1, wherein the dye compound is an oxonol compound having the following formula (IV-1) or (IV-2):

in which each of A³ ₁, A⁴, B³ and B⁴ independently represents a substituent group selected from the group consisting of a linear, branched or cyclic alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, an aryl group having 6 to 18 carbon atoms, an aralkyl group having 7 to 18 carbon atoms, an acyl group having 2 to 18 carbon atoms, an alkylsulfonyl group having 1 to 18 carbon atoms, an arylsulfonyl group having 6 to 18 carbon atoms, an alkylsulfinyl group having 1 to 18 carbon atoms, an alkoxycarbonyl group having 2 to 18 carbon atoms, an aryloxycarbonyl group having 7 to 18 carbon atoms; an alkoxy group having 1 to 18 carbon atoms, an aryloxy group having 6 to 18 carbon atoms, an alkylthio group having 1 to 18 carbon atoms, an arylthio group having 6 to 10 carbon atoms, an acyloxy group having 2 to 18 carbon atoms, a sulfonyloxy group, a carbamoyloxy group, an amino group, a carbamoyl group, a sulfamoyl group, a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxyl group, and a 4- to 7-membered heterocyclic group, wherein these substituent groups may be substituted with at least one group selected from those consisting of the above-mentioned substituent groups; each of Y² and Z² independently represents a group of atoms required for forming a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring, which may be substituted with at least one group selected from those consisting of the substituent groups described for A³, A⁴, B³ and B⁴ and may be fused with a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring; each of L⁶, L⁷, L⁸, L⁹ and L¹⁰ independently represents a methine group which may have one or two substituent groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴; M²⁺ represents a quaternary ammonium ion; and each of m1 and n1 independently represents an integer of 0, 1 or
 2. 7. The information recording medium of claim 6, wherein M²⁺ is an ion having the following formula (V):

in which each of R¹¹ and R¹² independently represents a group selected from the group consisting of an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); each of R¹³ and R¹⁴ independently represents a substituent group selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹¹ and R¹³, R¹² and R¹⁴, or R¹³ and R¹⁴ can be combined to form a 4- to 7-membered ring; each of q3 and r3 independently is an integer of 0 to 4; provided that plural R¹ and plural R¹⁴ are the same as or different from each other in the case that q3 and r3 are 2 or more, respectively.
 8. The information recording medium of claim 6, wherein M²⁺ is an ion having the following formula (VI):

in which each of R¹⁵ and R¹⁶ independently represents a group selected from the group consisting of an alkyl, group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); each of R¹⁷ and R¹⁸ independently represents a substituent group selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹⁵ and R¹⁶, R¹⁵ and R¹⁷ R¹⁶ and R¹⁸ or R¹⁷ and R¹⁸ can be combined to form a 4- to 7-membered ring; each of q4 and r4 independently is an integer of 0 to 4; provided that plural R¹⁷ and plural R¹⁸ are the same as or different from each other in the case that q4 and r4 are 2 or more, respectively.
 9. The information recording medium of claim 1, wherein each of m and n is 1; m is 0, while n is 2; or m is 2, while n is
 0. 10. The information recording medium of claim 1, wherein X¹ is ═O and X² is —O.
 11. The information recording medium of claim 1, wherein a light-reflecting layer is provided on the recording layer.
 12. An oxonol compound having the following formula (IV-1) or (IV-2):

in which each of A³, A⁴, B³ and B⁴ independently represents a substituent group selected from the group consisting of a linear, branched or cyclic alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, an aryl group having 6 to 18 carbon atoms, an aralkyl group having 7 to 18 carbon atoms, an acyl group having 2 to 18 carbon atoms, an alkylsulfonyl group having 1 to 18 carbon atoms, an arylsulfonyl group having 6 to 18 carbon atoms, an alkylsulfinyl group having 1 to 18 carbon atoms, an alkoxycarbonyl group having 2 to 18 carbon atoms, an aryloxycarbonyl group having 7 to 18 carbon atoms; an alkoxy group having 1 to 18 carbon atoms, an aryloxy group having 6 to 18 carbon atoms, an alkylthio group having 1 to 18 carbon atoms, an arylthio group having 6 to 10 carbon atoms, an acyloxy group having 2 to 18 carbon atoms, a sulfonyloxy group, a carbamoyloxy group, an amino group, a carbamoyl group, a sulfamoyl group, a halogen atom, a hydroxyl group, a nitro group, a cyano group, a carboxyl group, and a 4- to 7-membered heterocyclic group, wherein these substituent groups may be substituted with at least one group selected from those consisting of the above-mentioned substituent groups; each of Y² and Z² independently represents a group of atoms required for forming a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring, which may be substituted with at least one group selected from those consisting of the substituent groups described for A³, A⁴, B³ and B⁴ and may be fused with a 4- to 7-membered carbon ring or a 4- to 7-membered heterocyclic ring; each of L⁶, L⁷, L⁸, L⁹ and L¹⁰ independently represents a methine group which may have one or two substituent groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴; M²⁺ represents a quaternary ammonium ion; and each of m1 and n1 independently represents an integer of 0, 1 or
 2. 13. The oxonol compound of claim 12, wherein M²⁺ is an ion having the following formula (V):

in which each of R¹¹ and R¹² independently represents a group selected from the group consisting of an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); each of R¹ and R¹⁴ independently represents a substituent group selected from the group consisting of the substituent groups described for A³, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹¹ and R¹³, R¹² and R¹⁴, or R¹³ and R¹⁴ can be combined to form a 4- to 7-membered ring; each of q3 and r3 independently is an integer of 0 to 4; provided that plural R¹³ and plural R¹⁴ are the same as or different from each other in the case that q3 and r3 are 2 or more, respectively.
 14. The oxonol compound of claim 12, wherein M²⁺ is an ion having the following formula (VI):

in which each of R¹⁵ and R¹⁶ independently represents a group selected from the group consisting of an alkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18 carbon atoms, an alkynyl group having 2 to 18 carbon atoms, and an aryl group having 6 to 18 carbon atoms, wherein the alkyl, alkenyl, alkynyl and aryl group may be substituted with one or more groups selected from the group consisting of the substituent groups described for A³, A⁴, B and B⁴ of the formulas (IV-1) or (IV-2); each of R¹⁷ and R¹⁸ independently represents a substituent group selected from the group consisting of the substituent groups described for A³ ₁, A⁴, B³ and B⁴ of the formulas (IV-1) or (IV-2); or each set of R¹⁵ and R¹⁶, R¹⁵ and R¹⁷, R¹⁶ and R¹⁸, or R¹⁷ and R¹⁸ can be combined to form a 4- to 7-membered ring; each of q4 and r4 independently is an integer of 0 to 4; provided that plural R¹⁷ and plural R¹⁸ are the same as or different from each other in the case that q4 and r4 are 2 or more, respectively.
 15. The oxonol compound of claim 12, wherein each of m1 and n1 is 1; m1 is 0, while n1 is 2; or m1 is 2, while n1 is
 0. 16. The oxonol compound of claim 12, wherein each of the carbon ring and the heterocyclic ring for the group of atoms represented by Y² or Z² is selected from the group consisting of pyrazolone ring, ring of thiobarbituric acid, ring of barbituric acid, indandione ring and hydroxyphenalenone ring. 